Studies on waterline corrosion processes and corrosion product characteristics of carbon steel in 3.5 wt% NaCl solution

The waterline corrosion behaviors of carbon steel partially immersed in a 3.5 wt% NaCl solution were investigated using the wire beam electrode technique, and the effects of corrosion products on the processes of waterline corrosion were analyzed. The results demonstrated that the initial stage and development stage of waterline corrosion were mainly controlled by the concentration and diffusion of dissolved oxygen, respectively, and the deceleration stage of waterline corrosion was mainly affected by corrosion products. The main component of the yellow corrosion products was γ-FeOOH, and γ-FeOOH that exhibited a high reduction reactivity could be involved in the cathodic reaction. The black corrosion products were mainly composed of Fe₃O₄ with strong thermodynamic stability and the processes of dissolved oxygen diffusion and ion transports were obviously affected due to the continuous accumulation of Fe₃O₄ on the surface of the electrodes. Polarity reversals were observed on the single electrodes below the waterline, but the reasons for the phenomena were different from each other.     

One-step preparation of the superhydrophobic Al alloy surface with enhanced corrosion and wear resistance

Corrosion and wear failures are bottlenecks for restricting applications and developments of Al-based functional materials. As a new lubrication technology, superhydrophobic preparation provides an effective way to settle Al alloy corrosion. The preparation methods of superhydrophobic Al alloys are mainly multistep strategies. In this study, superhydrophobic Al alloy, has been prepared by an efficient one-step electrochemical etching process. Meanwhile, its micromorphology has been observed by a scanning electron microscope. The wettability has been measured by video optical contact angle meter. The corrosion behavior has been tested by electrochemical workstation, and wear performance has been characterized by friction tester. The results show that the micro-nanoterraced concave–convex structure has been fabricated and an as-prepared surface exhibits excellent superhydrophobic behavior. Further electrochemical and tribological tests show that corrosion resistance and wear resistance have also been significantly improved. This study provides a new method to prepare wear-resistant and corrosion-resistant Al alloy for widening applications of multifunctional Al-based engineering materials.     

气藏型储气库注气期试井分析探讨

针对气藏型储气库注采井注采过程中储层物性参数影响因素不明确、注采能力不对称的问题。基于相国寺储气库井下连续油管试井测试结果,提出储气库注气期“温降效应”、“变表皮效应”的概念,分析了储气库注采过程中温降效应、变表皮效应以及储层应力敏感对注采的影响。通过气藏型储气库注气期试井分析技术,研究各因素在试井曲线上的响应特征以及对试井解释参数的影响。结果表明:①相对于采气期试井测试,注气期测试得到的储层物性参数具有同样的参考价值;②储气库温降效应对于试井解释结果的影响可忽略不计,而在不同注采运行周期内,变表皮效应以及应力敏感效应影响差异较大;③编制储气库注采运行方案时应充分考虑变表皮效应与应力敏感的影响,在不同注采运行周期内开展试井测试获取准确的储层参数值。研究成果为储气库试井测试与解释提供了重要的研究依据和理论指导。     

钕铁硼化学镀防护及在模拟海洋大气环境中的腐蚀行为

采用化学镀方法在钕铁硼表面分别制备Ni-P合金镀层、Ni-Mo-P合金镀层、Ni-P/PTFE复合镀层和Ni-Mo-P/PTFE复合镀层,并研究了不同化学镀层在模拟海洋大气环境中的腐蚀行为。结果表明:Ni-P合金镀层、Ni-Mo-P合金镀层、Ni-P/PTFE复合镀层和Ni-Mo-P/PTFE复合镀层都完整覆盖钕铁硼表面,它们的粗糙度差别不大,在模拟海洋大气环境中的腐蚀失重都低于钕铁硼的腐蚀失重,容抗弧半径增大且电荷转移电阻有不同程度的提高。与Ni-P合金镀层和Ni-Mo-P合金镀层相比,Ni-P/PTFE复合镀层和Ni-Mo-P/PTFE复合镀层具有优良的耐腐蚀性能,原因在于PTFE颗粒较均匀的沉积在镀层表面增加一道屏蔽层,也起到阻碍腐蚀介质渗透腐蚀的作用。尤其是Ni-Mo-P/PTFE复合镀层,其表面更致密,PTFE颗粒沉积更均匀,能更有效延缓腐蚀介质与钕铁硼接触,显著提高钕铁硼在模拟海洋大气环境中的耐腐蚀性能。     

超厚板TC4钛合金电子束焊接接头应力腐蚀敏感性

针对100 mm超厚板TC4钛合金电子束焊接接头，采用慢应变速率拉伸方法评价接头在人造海水中的应力腐蚀敏感性，分析接头的显微组织和断口形貌，对接头的腐蚀机制进行研究. 结果表明，室温条件下应变速率为ε=1×10-6 s-1时，母材在海水中未表现出应力腐蚀敏感性；焊缝上部、中部和下部具有轻微应力腐蚀敏感性. 焊缝在海水中发生阳极溶解，产生氢吸附，导致裂纹的萌生. 同时氢扩散诱导α'相界及α'相内发生位错塞积，进而使裂纹在更低的应力水平下发生扩展.     

The influence of volume fraction of amorphous phase on corrosion resistance of Mg67Zn 29Ca 4 alloy

The aim of this study was to investigate the structure and corrosion resistance of amorphous, amorphous‐crystalline, and crystalline Mg₆₇Zn₂₉Ca₄ alloy for biodegradable applications. This paper presents a preparation method and results of the structural characterization and corrosion resistance analysis of the material. Samples were prepared in the form of 3 mm diameter rods. The structure of the alloy was examined with the use of X‐ray diffractometry and scanning electron microscopy. The thermal properties of the samples were examined with differential scanning calorimetry (DSC). Results of DSC analysis were used to determine heat treatment temperatures, allowing to obtain different fractures of crystalline phase in the material. Corrosion resistance of heat‐treated samples was investigated by immersion tests and electrochemical measurements performed in the simulated body fluid. The X‐ray diffraction results confirmed that the prepared Mg₆₇Zn₂₉Ca₄ alloy's structure is fully amorphous. After heat treatment, samples with different fractions of amorphous phase in the structure were obtained. Immersion tests of the samples showed that the structure significantly influenced corrosion resistance in examined materials. It should be pointed out, that certain amounts of crystalline phase in amorphous matrix can greatly improve the corrosion resistance of Mg₆₇Zn₂₉Ca₄ alloy.     

蜂窝梁的稳定性能研究进展

对蜂窝梁破坏模式的研究表明，失稳是其结构性能失效的重要破坏模式。为此，在回顾蜂窝梁结构特性研究的基础上，总结归纳了蜂窝梁失稳的3种主要模式：整体弯扭失稳、梁墩屈曲、畸变屈曲。结合国内外近30多年来对蜂窝梁稳定性的试验研究成果，对影响蜂窝梁稳定性的主要因素进行分析。采用蒙特卡洛法得到纯弯简支蜂窝梁弯扭失稳临界荷载的概率分布和影响因子的敏感度。将部分具有代表性的试验成果与欧洲规范EN 1993-1-1计算结果进行对比，根据中国规范GB 50068—2001《建筑结构可靠度设计统一标准》提供的抗力分项系数，计算了不同荷载组合下蜂窝梁整体弯扭失稳临界荷载的可靠度指标，为国内规范的制订提供依据。最后，总结了当前蜂窝梁稳定性研究中存在的不足，指明了进一步研究的方向。